蒸压加气混凝土砌块辐射防护屏蔽性能试验研究

辐射防护 ›› 2020, Vol. 40 ›› Issue (2): 110-114.

蒸压加气混凝土砌块辐射防护屏蔽性能试验研究

陆洋^1,3 ,张永贵², 杜中³, 陈志¹, 陶宗硕²

1.中国科学技术大学物理学院,合肥 230027;
2.中国建材检验认证集团安徽有限公司,合肥 230000;
3.合肥市环境监测中心站,合肥 230000

收稿日期:2019-10-12 发布日期:2020-05-15
通讯作者: 陈志。E-mail:zchen@ustc.edu.cn
作者简介:陆洋(1989—),男,2012年毕业于南华大学核技术专业,工程师。E-mail:ranger_u@163.com

Experimental research on radiation protection shielding performance of autoclaved aerated concrete blocks

LU Yang^1,3, ZHANG Yonggui², DU Zhong³ , CHEN Zhi¹, TAO Zongshuo²

1. College of Physics, University of Science and Technology of China, Hefei 230027;
2. China Building Material Inspection and Certification Group Anhui Co. Ltd. , Hefei 230000;
3. Hefei Environmental Monitoring Center Station, Hefei 230000

Received:2019-10-12 Published:2020-05-15

摘要/Abstract

摘要： 本文利用相同管电流(25 mA)不同管电压(70 kV~120 kV)下产生的X射线,对国内4种常用蒸压加气混凝土砌块样品进行照射,并测量射线穿过每种样品后固定点位处的空气吸收剂量率。研究得出:(1)在70 kV～120 kV条件下,蒸压加气混凝土砌块的等效铅当量厚度随着管电压的增加出现先增加后减小的变化趋势,在90 kV时达到最大;(2)4种蒸压加气混凝土砌块的等效铅当量厚度均大于1.0 mm,部分射线装置机房可选用蒸压加气混凝土作为辐射防护材料;(3)蒸压加气混凝土砌块的等效铅当量厚度与材料的干密度、厚度有关,与抗压强度无关,材料的干密度越大、材料厚度越大,等效铅当量厚度越高。

关键词: 蒸压加气混凝土砌块, 辐射防护, 等效铅当量厚度

Abstract: In this paper, using X-rays generated at different tube voltages (70 kV to 120 kV) with the same tube current (25 mA), four commonly used autoclaved aerated concrete block samples in China were irradiated and the air absorption dose rate was measured at the fixed point after the X-rays passed through each sample. The results show that: (1) the equivalent lead equivalent thickness of autoclaved aerated concrete block under the condition of 70 kV to 120 kV increases first and then decreases with the increase of tube voltage, reaching the maximum at 90 kV (2) the equivalent lead equivalent thickness of four kinds of autoclaved aerated concrete blocks is more than 1.0 mm, and autoclaved aerated concrete can be used as radiation protection material in some machine rooms (3) the equivalent lead equivalent thickness of autoclaved aerated concrete block is related to the dry density and thickness of the material, which is independent of compressive strength.

Key words: autoclaved aerated concrete block, radiation protection, equivalent lead equivalent thickness

中图分类号:

TL77

陆洋 ,张永贵, 杜中, 陈志, 陶宗硕. 蒸压加气混凝土砌块辐射防护屏蔽性能试验研究[J]. 辐射防护, 2020, 40(2): 110-114.

LU Yang, ZHANG Yonggui, DU Zhong , CHEN Zhi, TAO Zongshuo. Experimental research on radiation protection shielding performance of autoclaved aerated concrete blocks[J]. RADIATION PROTECTION, 2020, 40(2): 110-114.

[1]	姚振, 赵敏艳, 刘玉龙. 红外热成像技术在辐射防护及其他医学领域中的应用[J]. 辐射防护, 2020, 40(1): 78-83.
[2]	刘显荣, 何丽艳, 卢先州. 姜黄素对辐射诱导的胰腺外分泌细胞损伤的保护作用[J]. 辐射防护, 2019, 39(2): 157-167.
[3]	秦秀军, 孙鸽, 岳娟, 黄立群, 李炜宾, 尹晶晶, 李建国. 富氢水对⁶⁰Co照射比格犬急性血液系统损伤的保护作用研究[J]. 辐射防护, 2018, 38(5): 428-432.
[4]	陈梦, 张菊红, 张杰, 王琤, 李海兵. 基于PET/CT中心的辐射监测及放射防护评价[J]. 辐射防护, 2018, 38(3): 212-216.
[5]	贾林胜, 冯宗洋, 杨亚鹏, 徐潇潇, 张建岗, 王宁. 辐射防护最优化参数α值的最新估算[J]. 辐射防护, 2018, 38(3): 246-251.
[6]	钟春明, 岳中慧, 张鑫. 工业电缆电子辐照加速器辐射防护评价[J]. 辐射防护, 2018, 38(1): 33-37.